LNP™ STAT-KON™ LX00797C compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MWInf3_LNP-STAT-KON-LX00797C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-KON* LX00797C is a compound based on Polyetheretherketone containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-L-00797 CCS Product reorder name: LX00797C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 155 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 7930 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 195 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 310 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 to 1.0E+6 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rulon® LR | Saint Gobain Performance Plastics | PTFE | Rulon® |
| DESLON™ 66 DSC201GW3 | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| Ebalta AH 120 / TGL | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| Karina BEIGE PVC COMP. -E 856-08/435-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| Sylvin 9766-83 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |