Makrolon® Solid Sheet GP
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® Solid Sheet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MVLAk2_MakrolonSolidSheetGP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Solid Makrolon® sheets are clear, polished, UV-stabilized polycarbonate sheets. They offer extreme impact strength that exceeds the physical properties of other products of their class. Makrolon® sheets resist temperatures of -100 to +120°C, exhibit high optical clarity and have a good fire rating. Makrolon® GP clear 099 is a clear transparent sheet with high light transmission. Makrolon® NR clear 099 is a transparent sheet with a matt finish and improved UV resistance on one side. Makrolon® GP white 130 and white 150 are translucent sheets offering good light diffusion combined with a pleasant white color. Makrolon® GP umbra 775 sheets are brown-colored and transparent. Makrolon® FG clear 099 is a clear transparent sheet suitable for food-contact and medical applications. Applications: Typical applications for Makrolon® GP sheets include machine guards, lighting fixtures, signs, wall and door partitions. The sheets offer protection against involuntary breakage and wilfull destruction. Makrolon® GP sheets can be thermoformed, cold-curved and machined with ease. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | > 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2350 | MPa | ISO 178 |
| Flexural Stress 2 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C, Partial Break) | 80 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact 4(23°C, Partial Break) | 90 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 128 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 148 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.20 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 34 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.10 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 5.0E-4 | ASTM D150 | |
| 1 MHz | 9.5E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| > 1.5 mm, ALL | HB | UL 94 | |
| 0.8 to 1.4mm, ALL | V-2 | UL 94 | |
| > 10.0 mm, Clear 009 | V-0 | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Refractive Index 5 | 1.587 | ISO 489 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 3 mm |
| 4 . | 3.2 mm |
| 5 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYVIN® PVC 6528E | A. Schulman Inc. | PVC, Unspecified | POLYVIN® |
| Fitex PPS 1340L | Kotec Corporation | PPS | Fitex PPS |
| Hanwha Total PP HS120 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| LNP™ KONDUIT™ PX13012 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ KONDUIT™ |
| PermaStat® 600 MD | RTP Company | ABS | PermaStat® |