SCHULAMID® 6 MV 14 FR
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MUmiyq_SCHULAMID-6-MV-14-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viskosity flame-retardant Polyamide 6 grade;halogen- and phosphorus-free |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.17 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3400 | 1100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 80.0 | 38.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.0 | 28 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 8.0 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 80.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 220 | -- | °C | ISO 306/A50 |
| -- | 205 | -- | °C | ISO 306/B50 |
| Ball Pressure Test (200°C) | Pass | -- | IEC 60695-10-2 | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 80.0 | -- | °C | |
| 1.50 mm | 85.0 | -- | °C | |
| 3.00 mm | 85.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 105 | -- | °C | |
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 155 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.750 mm | PLC 3 | -- | ||
| 1.50 mm | PLC 3 | -- | ||
| 3.00 mm | PLC 2 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | ISO 3795 | |||
| 0.750 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| 1.50 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| 3.00 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.750 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- | ||
| 3.00 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 700 | -- | °C | |
| 1.50 mm | 700 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| Oxygen Index | 31 | -- | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multiuse Leostomer® LE-3140N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| Dryflex® 502400S | ELASTO | SEBS | Dryflex® |
| Eastar™ EN058, Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| Eltex® PF6220AA | INEOS Olefins & Polymers Europe | mLLDPE | Eltex® |
| Leona™ 1300G | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |