ULTEM™ 6202 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MU5TgH_ULTEM-6202-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
12% Silica filled, standard flow Polyetherimide Copolymer (Tg 235C). ECO Conforming, UL94 VO Listing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (367°C/6.6 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (24 hr) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 96.5 | MPa | |
| Break | 92.4 | MPa | |
| Tensile Elongation 2(Break) | 10 | % | ASTM D638 |
| Flexural Modulus 3(100 mm Span) | 4410 | MPa | ASTM D790 |
| Flexural Strength 4 | ASTM D790 | ||
| Yield, 100 mm Span | 145 | MPa | |
| Break, 100 mm Span | 145 | MPa | |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 11.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 370 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 214 | °C | ASTM D648 |
| Vicat Softening Temperature | 237 | °C | ASTM D1525 5 |
| CLTE | ASTM E831 | ||
| Flow : -20 to 150°C | 4.5E-5 | cm/cm/°C | |
| Transverse : -20 to 150°C | 4.9E-5 | cm/cm/°C | |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI Str | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm, in Oil) | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.10 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 1.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.47 mm) | V-0 | UL 94 | |
| Oxygen Index | 48 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 360 to 382 | °C | |
| Middle Temperature | 371 to 393 | °C | |
| Front Temperature | 382 to 404 | °C | |
| Nozzle Temperature | 377 to 399 | °C | |
| Processing (Melt) Temp | 382 to 404 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mytex® AS172LW-01US | Mytex Polymers | TPO | Mytex® |
| Geon™ Vinyl Rigid Extrusion 87547 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Kepamid® 2300ST | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| KumhoSunny PC/ABS HAC8250TC | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Karina COMP. PVC WHITE -E 800-10/ 1-CY-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |