LNP™ THERMOCOMP™ LC008EXQ compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MTFL2L_LNP-THERMOCOMP-LC008EXQ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LC008EXQ is a compound based on Polyetheretherketone containing 40% Carbon Fiber. Added features of this grade include: Electrically Conductive, Easy Molding. Also known as: LNP* THERMOCOMP* Compound LC008EXQ Product reorder name: LC008EXQ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.15 to 0.30 | % | |
| Across Flow : 24 hr | 0.70 to 1.4 | % | |
| Water Absorption (24 hr, 50% RH) | 0.050 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 41500 | MPa | ASTM D638 |
| -- | 40400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 330 | MPa | ASTM D638 |
| Break | 321 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.5 | % | ASTM D638 |
| Break | 1.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 35200 | MPa | ASTM D790 |
| -- 5 | 33800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 460 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 492 | MPa | ASTM D790 |
| Compressive Strength | 215 | MPa | Internal Method |
| Shear Modulus | 5000 | MPa | ASTM C273 |
| Shear Strength | 126 | MPa | ASTM C273 |
| Poisson's Ratio | 0.47 | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 82 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 860 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 7.20 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 335 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC101E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| TOTAL Polystyrene Impact 625 | TOTAL Refining & Chemicals | PS (MIPS) | TOTAL Polystyrene |
| ALKAMIX™ MB6003 | Qenos Pty Ltd | LLDPE | ALKAMIX™ |
| Electrafil® POM 04008 mb | Techmer Engineered Solutions | Acetal (POM) Copolymer | Electrafil® |
| POCAN® KU 2-7003 POS042 000000 | LANXESS GmbH | PBT | POCAN® |