ULTEM™ SF2250 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MS0U4T_ULTEM-SF2250-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow ULTEM for thin wall application |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 20 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (345°C/10.0 kg) | 40.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.46 | % | |
| Across Flow | 0.54 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8900 | MPa | ASTM D638 |
| Tensile Strength | |||
| Break 2 | 162 | MPa | ASTM D638 |
| Break | 157 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 7260 | MPa | ASTM D790 |
| -- 5 | 7150 | MPa | ISO 178 |
| Flexural Strength 6(Yield, 50.0 mm Span) | 197 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 89 | J/m | ASTM D256 |
| 23°C 7 | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 203 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 8 | 208 | °C | ISO 75-2/Ae |
| CLTE | |||
| Flow : -40 to 150°C | 1.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 150°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 150°C | 5.9E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 381 TFE 10 | RTP Company | PC | RTP |
| SABIC® PPcompound 6614 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Mylar® S (92 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Kuraray Poval® PVA 205 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| TechnoDur PBT4 GF 30 Natural (9987) | TechnoCompound GmbH | PBT | TechnoDur |