FORMULA P ELAN XP 422
| Category: | PP+Styrenic , Polypropylene + Styrenic |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MRowV3_FORMULA-P-ELAN-XP-422.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP/.PS-Blend. This material has very good scratch-resistance. This type has the same shrinkage like PP with 20% mineral with a 10% lower density. Low warpage and no wear on mold surface. New: high impact at -20°C. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 - 1.2 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 22.0 | MPa | ISO 527-2 |
| Fracture | 19.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 80 | % | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 42.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -20°C | 4.0 | kJ/m² | ISO 180 |
| 23°C | 15 | kJ/m² | ISO 180 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Heat Aging (150°C) | 16.7 | day |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 67.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 22 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 250 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Crystal 1450N | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| Arak HDPE BL4 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| Fiberfil® J-60/20/E/NS | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Ebalta AH 120 / GL | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| ICORENE® 4140 | ICO Polymers SA, A Division of A. Schulman | PE Copolymer | ICORENE® |