Next Nylon 6 Industrial Series NG30-02ABK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Industrial Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MR6N4Z_Next-Nylon-6-Industrial-Series-NG30-02ABK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Glass Fiber Reinforced Black compound Product Applications This grade is used for industrial and electrical insulating parts and Heavy duty application such as brake fluid reservoir, pillon handels, gears, cams, chair base etc Benefits Good Balance Strength, stiffness and thermal property with excellent moldability/surface aesthetics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.30 | -- | % | |
| Across Flow | 0.85 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.2 | -- | % | |
| Saturation 1 | 7.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 105 | -- | ||
| R-Scale | 125 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 140 | 95.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 6.0 | % | ASTM D638 |
| Flexural Modulus | 8500 | -- | MPa | ASTM D790 |
| Flexural Strength | 210 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 98 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 215 | -- | °C | |
| 1.8 MPa, Unannealed | 190 | -- | °C | |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 25 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800 D-75A | RTP Company | TPO (POE) | RTP |
| Mediprene® A2 500550M | ELASTO | SEBS | Mediprene® |
| VITAMIDE® BS10VN6607 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| NEFTEKHIM PP 1421J (T38CA) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| ELASTOSIL® AUX BATCH PT 2 | Wacker Chemie AG | Silicone | ELASTOSIL® AUX |