Next Nylon 66 Prime Series PST-01BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MR4rfO_Next-Nylon-66-Prime-Series-PST-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 UnFilled Super Tough Black Compound Product Applications This grade is widely used for: Sports and leisure applications ski component, ski and surf binding, Toy application such as bumper of remote controlled car and battery gasket, Fastners etc Benefits High impact resistance even at low temperature |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.08 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.5 | -- | % | |
| Across Flow | 1.5 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.2 | -- | % | |
| Saturation 1 | 6.2 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 70 | -- | ||
| R-Scale | 105 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 62.0 | 44.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | > 50 | % | ASTM D638 |
| Flexural Modulus | 2000 | 1100 | MPa | ASTM D790 |
| Flexural Strength | 78.0 | 70.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | -- | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 135 | -- | °C | |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | |
| Melting Temperature | 260 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3457 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| MonoSol® M8630 - 2 mil | MonoSol, LLC | PVOH | MonoSol® |
| CP PRYME® Acetal AC100-9 | Chase Plastics Services Inc. | Acetal (POM) Copolymer | CP PRYME® Acetal |
| Ferro PP TPP40AC50HB-BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Generic ABS+PC - Carbon Fiber, Nickel-Coated | Generic | PC+ABS | Generic |