Next Nylon 6 Prime Series NX-01GY
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MR2Tgu_Next-Nylon-6-Prime-Series-NX-01GY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 UnFilled Grey Compound Product Applications Generally recommended for Industial and Automobile Application Benefits It provides a combination of strength, stiffness and toughness properties |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.13 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.2 | -- | % | ASTM D955 |
| Transverse flow | 1.2 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.3 | -- | % | ASTM D570 |
| Saturation 1 | 8.5 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 90 | -- | ASTM D785 | |
| Class r | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 70.0 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | > 50 | % | ASTM D638 |
| Flexural Modulus | 2700 | 2100 | MPa | ASTM D790 |
| Flexural Strength | 105 | 90.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | 78 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 180 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 75.0 | -- | °C | ASTM D648 |
| Melting Temperature | 222 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 260 - 270 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BZM-23 BLK TL | Arkema | Nylon 11 | Rilsan® |
| RTP 225 Z | RTP Company | Nylon 66 | RTP |
| Radilon® S 40E 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| Hifax TYC 007P E C13097 | LyondellBasell Industries | PP Copolymer | Hifax |
| Polimid A SG/5 | Poliblend S.p.a. | Nylon 66 | Polimid A |