PLUSTEK PA507
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MQOySu_PLUSTEK-PA507.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FLAME RETARDANT POLYAMIDE 6.6 FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 1.0 - 1.4 | % | ASTM D955 |
| -- | 1.0 - 1.4 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 7.5 | % | ASTM D570 |
| Saturated, 23°C | 7.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.5 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 80.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 15 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 120 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 30 | J/m | ASTM D256 |
| 23°C | 30 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 95.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 220 | °C | ASTM D648, ISO 75-2/A |
| Maximum Service Temperature | |||
| -- 1 | > 180 | °C | |
| -- | 100 | °C | |
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 70 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.30 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 285 - 310 | °C | |
| Mold Temperature | 65.0 - 110 | °C | |
| Injection Pressure | 70.0 - 125 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Note Message | |
|---|---|
| 1 . | Short Peaks Operation |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP251 | Southern Polymer, Inc. | PP Impact Copolymer | PRIMALENE |
| PRL PPX-GP5 | Polymer Resources Ltd. | PPE+PS | PRL |
| BCC Resins BC 100 Thick | BCC Products Inc. | EA | BCC Resins |
| Chemical Resources PA612153HS | Chemical Resources, Inc. | Nylon 612 | Chemical Resources |
| LEXAN™ IR2840 resin | SABIC Innovative Plastics | PC | LEXAN™ |