Lifoflex® UV FLAM 60600
| Category: | SEBS , Thermoplastic Elastomer |
| Manufacturer: | Müller Kunststoffe GmbH |
| Trademark: | Lifoflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MQ8RLx_LifoflexUVFLAM60600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Base Material: TPS - SEBS Recycling: 100% recyclable Mould Shrinkage (linear): Approx. 0.75 - 2% depending on e.g. shape of the detail and placement of gate Characteristics: Halogen free flame retardant thermoplastic elastomer Service temperature: -50°C to 100°C Bonds to: PP, PE |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183/A |
| Molding Shrinkage | 0.75 - 2.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 3 sec) | 57 - 63 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow (Yield) | 5.50 | MPa | DIN 53504-S2 |
| Tensile Elongation - Across Flow (Break) | 840 | % | DIN 53504-S2 |
| Tear Strength | 18 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 21 | % | ISO 815 |
| 70°C, 22 hr | 49 | % | ISO 815 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -50 - 100 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (3.00 mm) | 850 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 180 - 230 | °C | |
| Middle Temperature | 180 - 230 | °C | |
| Front Temperature | 180 - 230 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 2 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 180 - 220 | °C | |
| Cylinder Zone 4 Temp. | 180 - 220 | °C | |
| Cylinder Zone 5 Temp. | 180 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MOSTEN MT 350 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| TEREZ PA 6.6 HT 7500 GF 50 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Unichem 5312 | Colorite Polymers | PVC, Flexible | Unichem |
| Hostacom EKS360N | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| LEXAN™ ML2010 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |