LNP™ STAT-KON™ DD0009XP compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MPtdpB_LNP-STAT-KON-DD0009XP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DD0009XP is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include:Electrically Conductive, Flame Retardant. Also known as Stat-Kon* D- FR. Also known as: LNP* STAT-KON* Compound D-FR Product reorder name: DD0009XP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.80 | % | |
| Across Flow : 24 hr | 0.70 | % | |
| Water Absorption (24 hr, 50% RH) | 0.18 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2830 | MPa | ASTM D638 |
| -- | 2810 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 62.8 | MPa | ISO 527-2/5 |
| Break 3 | 54.0 | MPa | ASTM D638 |
| Break | 57.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.2 | % | ASTM D638 |
| Yield | 4.2 | % | ISO 527-2/5 |
| Break 5 | 5.6 | % | ASTM D638 |
| Break | 7.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2830 | MPa | ASTM D790 |
| -- 7 | 2880 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 102 | MPa | ISO 178 |
| Break, 50.0 mm Span 8 | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 9 | 6.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 10 | 71 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.0 | J | ASTM D3763 |
| -- | 6.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 133 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 131 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 5.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 60°C | 5.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 to 1.0E+10 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.70 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 254 to 266 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 254 to 288 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 FRC 2 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| THERMOLAST® M TM9MED (Series: MC/tl) | KRAIBURG TPE | TPE | THERMOLAST® M |
| Cheng Yu N6G20 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| HiFill® PC 0144 TC-1 | Techmer Engineered Solutions | PC | HiFill® |
| 3M™ Dyneon™ PTFE Compound TF 8465 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |