POLYREX® PH-88
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MPbQMq_POLYREX-PH-88.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYREX® PH-88 is a High Impact Polystyrene product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 6.0 | g/10 min | |
| 220°C/10.0 kg | 16 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 60 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 84.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 27.0 | MPa | ISO 527-2/50 |
| Break | 22.0 | MPa | ISO 527-2/50 |
| 3.00 mm 1 | 23.5 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break, 3.00 mm 2 | 40 | % | ASTM D638 |
| Break | 56 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.00 mm 3 | 1960 | MPa | ASTM D790 |
| -- 4 | 1200 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.00 mm 5 | 37.3 | MPa | ASTM D790 |
| -- 6 | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -- | 11 | kJ/m² | ISO 179 |
| -- | 12 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | 100 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| 23°C, 3.00 mm | 98 | J/m | ASTM D256 |
| 23°C, 6.00 mm | 83 | J/m | ASTM D256 |
| -- | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 80.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 74.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 94.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 89.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ASTM D1525, ISO 306/A120 6 7 |
| -- | 96.0 | °C | ISO 306/A50 |
| -- | 87.0 | °C | ISO 306/B50 |
| -- | 89.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 180 to 200 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® N-261 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| WaterClear Ultra 10122 | DSM Somos® | Unspecified | WaterClear |
| TOTAL Polypropylene PPH 3051 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Karina GRAY PVC COMPOUND -E 680D18/487-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9600-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |