LNP™ LUBRICOMP™ OCL36A compound
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MOgsF1_LNPLUBRICOMPOCL36Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP OCL4036 is a compound based on PPS - Branched resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound OCL-4036 Product reorder name: OCL36A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (315°C/5.0 kg) | 4.00 - 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 24 hours | 0.95 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.19 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.050 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 25000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 153 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 0.70 | % | ISO 527-2/5 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 21200 | MPa | ISO 178 |
| 80°C | 20600 | MPa | ISO 178 |
| 120°C | 10200 | MPa | ISO 178 |
| 150°C | 7900 | MPa | ISO 178 |
| 200°C | 6100 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 261 | MPa | ISO 178 |
| -- 4 | 217 | MPa | ISO 178 |
| 80°C 5 | 212 | MPa | ISO 178 |
| 120°C 6 | 118 | MPa | ISO 178 |
| 150°C 7 | 94.0 | MPa | ISO 178 |
| 200°C 8 | 66.0 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.39 | ASTM D3702 Modified | |
| Flexural Strain at Break 9 | ISO 178 | ||
| -- | 1.3 | % | ISO 178 |
| 80°C | 1.3 | % | ISO 178 |
| 120°C | 2.3 | % | ISO 178 |
| 150°C | 2.4 | % | ISO 178 |
| 200°C | 2.4 | % | ISO 178 |
| Wear Factor - Washer | 19.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -40°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 12 | ISO 180/1U | ||
| -40°C | 23 | kJ/m² | ISO 180/1U |
| 23°C | 26 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 13 | |||
| 0.45 MPa, unannealed, 64.0mm span | 278 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 255 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 4.9E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1630 | J/kg/°C | ASTM E1269 |
| Thermal Conductivity | 0.36 | W/m/K | ASTM D5930 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+3 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.80 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | Yield |
| 6 . | Yield |
| 7 . | Yield |
| 8 . | Yield |
| 9 . | 2 mm/min |
| 10 . | 80*10*3 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mecoline S RDX 1203 F | Melos GmbH | TP, Unspecified | Mecoline |
| Vi-Chem PVC VNC50D-80I | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| Dow ENDURANCE™ HFDK-0587 BK | The Dow Chemical Company | Ethylene Copolymer | Dow ENDURANCE™ |
| Plaslube® PC CF15 TL6 BK | Techmer Engineered Solutions | PC | Plaslube® |
| LNP™ STAT-LOY™ A3000 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-LOY™ |