BIOPLAST® Wrap 100
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | BIOTEC GmbH & Co. KG |
| Trademark: | BIOPLAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MOF8gO_BIOPLAST-Wrap-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BIOPLAST WRAP 100 is BIOTEC's trademark for a completely new, plasticizer-free thermoplastic material, which allows the production of films with paper-like properties. As a result of plasticizer absence no material built-up or steam occurs during processing of BIOPLAST WRAP 100. The complete biodegradability and other functional properties of BIOPLAST WRAP 100 enable the converter to advance in production areas, which could not be reached with traditional thermoplastic materials or paper. The potato starch used for BIOPLAST WRAP 100 is native and not blended with plasticizer (which would be necessary for example to produce thermoplastic starch, TPS). BIOPLAST WRAP 100 therefore exhibits outstanding processing- and performance-characteristics as well as an excellent shelf life. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 to 1.50 | g/cm³ | ISO 1183/A |
| Apparent Density | 0.85 to 0.95 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 to 20 | g/10 min | ISO 1133 |
| Particle Size | 1.00 to 3.00 | mm | |
| Water Content | < 0.30 | % | Internal Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | > 10 | µm | ISO 2286-3 |
| Tensile Strength | ISO 527-3 | ||
| MD : 23°C, 10 µm | 10.0 to 20.0 | MPa | |
| TD : 23°C, 10 µm | 10.0 to 20.0 | MPa | |
| Oxygen Transmission Rate (Wet) (20 µm) | 1000 to 1500 | cm³/m²/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (20 µm) | 150 to 190 | g/m²/24 hr | ASTM F1249 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.20 to 1.40 | g/cm³ | ISO 1133 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1507 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Radilon® AGV 15 Black | Radici Plastics | Nylon 66 | Radilon® |
| Delta N66-100A L | Delta Polymers | Nylon 66 | Delta |
| FLEXCHEM™ 4051-02 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| Sylvin 6219-80 Red 6251 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |