CelloTherm™ T430
| Category: | CA , Cellulose Acetate |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | CelloTherm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MNRgCO_CelloTherm-T430.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Regenerated cellulose film (RCF), coated on both sides. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.20 | ||
| vs. Itself - Static | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 30 µm | > 3000 | MPa | |
| 1% Secant, TD : 30 µm | > 1500 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm | 125 | MPa | |
| TD : Yield, 30 µm | 70.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 22 | % | |
| TD : Break, 30 µm | 70 | % | |
| Seal Strength 1 | 2.2 | N/mm | Internal Method |
| Seal Initiation Temperature 2(30 µm) | 100 to 160 | °C | Internal Method |
| Oxygen Transmission Rate (Wet) 3(23°C, 30 µm, 0.0% RH) | 3.00 | cm³/m²/24 hr | ASTM F1927 |
| Water Vapor Transmission 4 | 370 | g/m²/24 hr | ASTM E96 |
| Film Gauge | 29.9 | µm | Internal Method |
| Yield (29.9 µm) | 23.3 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 29.9 µm) | 95 | ASTM D2457 | |
| Haze 5(29.9 µm) | 3.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | g(f)/38mm, 135°C, 0.5 secs, 69 kN/m² |
| 2 . | 0.5s dwell, 69 kN/m² |
| 3 . | RH: 0 to 5% |
| 4 . | 38°C, 90%RH |
| 5 . | 2.5° wide angle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titanvene™ LL3550UA | PT. TITAN Petrokimia Nusantara | MDPE | Titanvene™ |
| Next Nylon 6 Prime Series NG40-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Fainplast PVC PG 6016/1 | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| KPOL-HDPE HD K-0.60/960 | KPOL Chem Co. | HDPE | KPOL-HDPE |
| LUVOCOM® 6-7834 VP | Lehmann & Voss & Co. | Nylon 12 | LUVOCOM® |