NILSAN A GP
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | NILSAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MLXsal_NILSAN-A-GP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASA high flow grade designed for low thickness walls and parts with big dimensions. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (23°C, 3.20 mm) | 0.40 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.45 | % | ISO 62 |
| Saturated, 23°C | 1.7 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield) | 51.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.3 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2500 | MPa | ISO 178 |
| Flexural Stress 2 | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 96.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 3 | 85.0 | °C | IEC 60216 |
| Vicat Softening Temperature | 97.0 | °C | ISO 306/B50 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 240 - 280 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 3 hrs |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | Short term |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RMA 78 | Ronald Mark Associates, Inc. | PVC Homopolymer | RMA |
| apirex® MBL 25 M | API SpA | TPU-Polyether | apirex® |
| Pearlbond™ 123 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| TECACOMP® POM TRM natural 3758 | Ensinger GmbH | Acetal (POM) Homopolymer | TECACOMP® |
| Hostacom X M1 T01 105555 | LyondellBasell Industries | PP Copolymer | Hostacom |