KumhoSunny ABS HFA705G
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MLW3Ic_KumhoSunny-ABS-HFA705G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HFA705G is high gloss,paint free enviromental flame retardant ABS resin. It has high weather resistance and heat resistance properties. HFA705G is mainly used in frame and base of TV, sound panel,etc. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 45 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Flexural Strength | 55.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-1 | ||
| 2.10 mm | V-0 | ||
| 3.20 mm | V-0 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| CSA File No. | LS 66457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 165 to 175 | °C | |
| Middle Temperature | 185 to 195 | °C | |
| Front Temperature | 200 to 210 | °C | |
| Nozzle Temperature | 195 to 205 | °C | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8200-55UV Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vipel® F701-FBG-20 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| VALOX™ V9561 resin | SABIC Innovative Plastics Europe | PET | VALOX™ |
| Electrafil® J-3/CF/40 | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| OTECH PVC OC7018-Soles | OTECH Corporation | PVC, Unspecified | OTECH PVC |