ShinkoLite-P IR D-70
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | ShinkoLite-P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MKwLF6_ShinkoLite-P-IR-D-70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ShinkoLite-P IR D-70 is a Polymethyl Methacrylate Acrylic material. It is available in North America for extrusion or injection molding. Important attributes of ShinkoLite-P IR D-70 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 32 | ||
| R-Scale | 85 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 29.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 90 | % | ASTM D638 |
| Flexural Modulus | 1270 | MPa | ASTM D790 |
| Flexural Strength (Break) | 39.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| CLTE - Flow | 1.1E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1460 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 3.90 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 0.040 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 220 to 270 | °C | |
| Middle Temperature | 220 to 270 | °C | |
| Front Temperature | 220 to 270 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 78.4 to 137 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 200 to 220 | °C | |
| Cylinder Zone 2 Temp. | 230 to 250 | °C | |
| Cylinder Zone 3 Temp. | 230 to 250 | °C | |
| Die Temperature | 230 to 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borflow™ HL504FB | Borealis AG | PP Homopolymer | Borflow™ |
| Borealis PE LE0574 | Borealis AG | PE, Unspecified | Borealis PE |
| Cosmic DAP K77/6220F | Cosmic Plastics, Inc. | DAP | Cosmic DAP |
| Lion Idemitsu Composites PPS C-21OSF | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Hostacom X 437 S 100000 | LyondellBasell Industries | PP Homopolymer | Hostacom |