RTP PP 30 GF NAT

Category: PP, Unspecified , Polypropylene
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: MKpp7Z_RTP-PP-30-GF-NAT.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Value Product - Glass Fiber - Chemically Coupled
General Information
Filler / Reinforcement
  • Glass Fiber, 30% Filler by Weight
Features
  • Chemically Coupled
RoHS Compliance
  • Contact Manufacturer
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.12g/cm³ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)3.0g/10 minASTM D1238
Molding Shrinkage - Flow (3.20 mm)0.20 to 0.40%ASTM D955
MechanicalNominal ValueUnitTest Method
Tensile Modulus 6890MPaASTM D638
Tensile Strength 75.8MPaASTM D638
Tensile Elongation (Yield)4.0 to 5.0%ASTM D638
Flexural Modulus 5170MPaASTM D790
Flexural Strength 117MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.20 mm)80J/mASTM D256
Unnotched Izod Impact (3.20 mm)590J/mASTM D4812
FlammabilityNominal ValueTest Method
Flame Rating (1.50 mm, ** Values per RTP Company testing.)HBUL 94
Additional InformationNominal ValueUnit
Primary Additive 30%
InjectionNominal ValueUnit
Drying Temperature 79.4°C
Drying Time 2.0hr
Processing (Melt) Temp 191 to 232°C
Mold Temperature 32.2 to 65.6°C
Injection Pressure 68.9 to 103MPa
Resin Grade Manufacturer Category Trademark
TRILOY® 410 Samyang Corporation PC+PET TRILOY®
DENKA Transparent Polymer TE-30S Denka Company Limited ABS DENKA Transparent Polymer
Keltan® 9950C LANXESS Buna GmbH EPDM Keltan®
Piolen® P B50A19 PiO Kunststoffe GmbH & Co KG PP Homopolymer Piolen® P
Dow Corning® C6-540 Dow Corning Corporation Silicone Dow Corning®