E-RIALFILL H 07 55 C
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MKkWfh_E-RIALFILL-H-07-55-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer obtained by recycling of industrial scraps, 55% filler with calcium carbonate. Flowability specific for injection molding. Available in natural and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.85 | % | |
| Flow | 0.85 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.040 | % | ISO 62 |
| Ash Content | 55 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 17.0 | MPa | |
| Break, 23°C | 14.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 2.0 | % | |
| Break, 23°C | 45 | % | |
| Flexural Modulus 2(23°C) | 3600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 34.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 42 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 2.3 | kJ/m² | |
| 23°C | 2.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 114 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 to 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Geon™ Vinyl Flexible XV3887 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| KOPLA PC KBG1060F | KOPLA Co., Ltd. | PBT | KOPLA PC |
| Pacrel® 5365N-AC | Nanjing Jinling OPTA Polymer Co., Ltd. | TPE | Pacrel® |
| Hostacom EP3307 G82718 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 8200-75 White 1453 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |