LNP™ LUBRICOMP™ RX05487 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MKUxfQ_LNP-LUBRICOMP-RX05487-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RX05487 is a compound based on Nylon 66 containing 10% Aramid Fiber, 10% Lubricant. Added features of this material are: Low Warpage, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RAL-4722 LW Product reorder name: RX05487 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.73 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3710 | MPa | ASTM D638 |
| -- | 3620 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 81.8 | MPa | ASTM D638 |
| Yield | 79.8 | MPa | ISO 527-2/5 |
| Break 3 | 81.8 | MPa | ASTM D638 |
| Break | 79.8 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 8.2 | % | ASTM D638 |
| Yield | 8.9 | % | ISO 527-2/5 |
| Break 5 | 8.3 | % | ASTM D638 |
| Break | 9.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3270 | MPa | ASTM D790 |
| -- 7 | 3330 | MPa | ISO 178 |
| Flexural Stress | 102 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.41 | ||
| vs. Itself - Static | 0.36 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.325 to 0.350 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 17.5 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 45 | J/m | ASTM D256 |
| 23°C 8 | 4.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 520 | J/m | ASTM D4812 |
| 23°C 9 | 37 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 1.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 249 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 235 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 144 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 116 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8334-60FU White 1510 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Braskem PP EP 548S | Braskem | PP Impact Copolymer | Braskem PP |
| Chiao Fu PA66 MD212G43 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| FRIANYL® A3 GF25 V0 | Nilit Plastics | Nylon 66 | FRIANYL® |
| HANWHA CP-430 | Hanwha Chemical | PVC Copolymer | HANWHA |