TECHNYL® A 216 S40 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MKGiBV_TECHNYL-A-216-S40-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, reinforced with 40% of glass spheres, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.4 | -- | % | |
| Flow | 1.4 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.70 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 1.00 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5000 | 3000 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 90.0 | 55.0 | MPa | |
| Break | 85.0 | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 4.0 | 20 | % | |
| Break | 15 | 35 | % | |
| Flexural Modulus | 4700 | 2450 | MPa | ISO 178 |
| Flexural Stress | 150 | 75.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 25 kJ/m² | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | 3.0 | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 6.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 5.0E+14 | 5.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 5.0E+14 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 28 | 26 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.11 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 500 | V | |
| Solution B | 500 | -- | V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 7059 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| YUNGSOX® PP 4084 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| Xuchuan XCS-3260DY | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Evermore PUR SS-302P | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Desmopan® DP 3072D | Covestro - PUR | TPU-Polyester | Desmopan® |