Kingfa API-CG338
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MInVGc_Kingfa-API-CG338.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa API-CG338 is a polypropylene material, and its filler is glass fiber reinforced material. This product is available in the Asia-Pacific region and is processed by injection molding. The main features of Kingfa API-CG338 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 - 19 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.90 | % | Internal method |
| Flow direction | 0.30 | % | Internal method |
| Ash Content (850°C) | 30 | % | ISO 3451-1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2/10 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/10 |
| Flexural Modulus 1 | 5200 | MPa | ISO 178 |
| Flexural Stress 2 | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 9.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm span | 156 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 147 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 200 - 230 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Processing (Melt) Temp | 220 - 245 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Processing Temp. Limit: 260°C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell Polyamide BH-18 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| Ebalta SG 198 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| ENGAGE™ 8450G | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| ESTABLEND 7600 | Cossa Polimeri S.r.l. | ASA+PC | ESTABLEND |
| LNP™ THERMOCOMP™ UX04509 compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |