VALOX™ VX4910 resin
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MHzGdg_VALOX-VX4910-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/3.8 kg | 20 | g/10 min | |
| 265°C/5.0 kg | 40 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 25.0 | cm³/10min | |
| 265°C/5.0 kg | 35.0 | cm³/10min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.80 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 100 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4600 | MPa | ASTM D638 |
| -- | 4600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 80.0 | MPa | ASTM D638 |
| Yield | 80.0 | MPa | ISO 527-2/5 |
| Break 3 | 80.0 | MPa | ASTM D638 |
| Break | 80.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Break 5 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3400 | MPa | ASTM D790 |
| -- 7 | 3800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 115 | MPa | ISO 178 |
| -- | 120 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 115 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 115 | MPa | ASTM D790 |
| Flexural Strain at Break 10 | 4.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 10 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 45 | J/m | ASTM D256 |
| 0°C | 50 | J/m | ASTM D256 |
| 23°C | 55 | J/m | ASTM D256 |
| -30°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| 0°C 12 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 13 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 340 | J/m | ASTM D4812 |
| 23°C | 440 | J/m | ASTM D4812 |
| -30°C 14 | 25 | kJ/m² | ISO 180/1U |
| 23°C 15 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 45.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 205 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 16 | 205 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 130 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 17 | 130 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 218 | °C | ASTM D1525, ISO 306/A50 11 18 |
| -- | 150 | °C | ASTM D1525, ISO 306/B50 12 19 |
| -- | 155 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.1E-5 | cm/cm/°C | |
| Flow : 23 to 60°C | 5.0E-5 | cm/cm/°C | |
| Flow : 23 to 150°C | 3.6E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.1E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.2E-4 | cm/cm/°C | |
| Transverse : 23 to 150°C | 2.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 3.40 | ASTM D150, IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150, IEC 60250 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 160 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 2 mm/min |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 mm |
| 17 . | 80*10*4 mm |
| 18 . | Rate A (50°C/h), Loading 2 (50 N) |
| 19 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8651-90 Clear 8289 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ARCEL® ULV (3.50 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| China PPS ha | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| Karina GRAY PVC COMPOUND 800-18/101-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ DF004 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |