Lupos® GP2305A
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupos® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MHUDtX_Lupos-GP2305A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose Applications Electric & Electronic (Housing, Components) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.10 - 0.20 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 108 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 8830 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 101 | °C | ASTM D648 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 220 - 235 | °C | |
| Middle Temperature | 220 - 240 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Nozzle Temperature | 230 - 245 | °C | |
| Processing (Melt) Temp | 235 - 245 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Back Pressure | 0.981 - 3.92 | MPa | |
| Screw Speed | 40 - 80 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4770 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SUPREME PP SPEXP56 | Supreme Petrochem Ltd. | PP, Unspecified | SUPREME PP |
| TAIRIPRO K8025 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| CP PRYME® Nylon 66 NN233HL-ES BK | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| PermaStat® 4005 | RTP Company | PPA | PermaStat® |