MEGOLON™ HF 8142 NATURAL
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | AlphaGary |
| Trademark: | MEGOLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MH6uEq_MEGOLON-HF-8142-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A FLEXIBLE, ZERO HALOGEN, 105°C RATED, FLAME RETARDED, THERMOPLASTIC OLEFINIC COMPOUND INTENDED FOR DEMANDING TELECOMMUNICATION CABLES. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 - 1.53 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 2.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 57 - 63 | ASTM D2240 | |
| Shaw D, 15 seconds | 48 - 54 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (0.762 mm) | 11.7 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 130 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 1(136°C, 168 hr) | -6.0 | % | UL Unspecified |
| Change in Ultimate Elongation in Air 2(136°C, 168 hr) | -13 | % | UL Unspecified |
| Change in Tensile Strength 3(70°C, 4 hr, in ASTM #2 Oil) | -29 | % | UL Unspecified |
| Change in Ultimate Elongation 4(70°C, 4 hr, in ASTM #2 Oil) | 22 | % | UL Unspecified |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -20.0 | °C | ASTM D746 |
| Hot pressing test- % Loss (80°C) | 20 | % | IEC 811-3-1 |
| Temperature index | > 355 | °C | NES 715 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | |||
| -- | 0 | % | MIL C-24643 |
| -- | mg/g | IEC 754-1 | |
| Smoke Index | 5.35 | NES 711 | |
| Toxicity | 4.60 | NES 713 | |
| Acid gas emission pH | 5.40 | IEC 60754-2 | |
| Acid gas emission conductivity | 0.380 | µS/mm | IEC 60754-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw Compression Ratio | 1.5:1.0 to 2.5:1.0 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant | ASTM D150 | ||
| 23°C, 1 MHz | 3.58 | ASTM D150 | |
| 23°C, 100 MHz | 3.49 | ASTM D150 | |
| 23°C, 200 MHz | 3.46 | ASTM D150 | |
| 23°C, 350 MHz | 3.45 | ASTM D150 | |
| 23°C, 600 MHz | 3.41 | ASTM D150 | |
| 23°C, 1.00 GHz | 3.38 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 23°C, 1 MHz | 0.022 | ASTM D150 | |
| 23°C, 100 MHz | 0.014 | ASTM D150 | |
| 23°C, 200 MHz | 0.012 | ASTM D150 | |
| 23°C, 350 MHz | 0.010 | ASTM D150 | |
| 23°C, 600 MHz | 8.5E-3 | ASTM D150 | |
| 23°C, 1.00 GHz | 7.9E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 44 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Cylinder Zone 1 Temp. | 154 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 166 | °C | |
| Cylinder Zone 4 Temp. | 171 | °C | |
| Cylinder Zone 5 Temp. | 171 | °C | |
| Adapter Temperature | 177 | °C | |
| Melt Temperature | 171 - 182 | °C | |
| Die Temperature | 177 | °C |
| Extrusion instructions |
|---|
| Barrier ScrewScreen Pack: 20/20 or 20/40 |
| Note Message | |
|---|---|
| 1 . | Thickness: 30 mil |
| 2 . | Thickness: 30 mil |
| 3 . | Thickness: 30 mil |
| 4 . | Thickness: 30 mil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom HDPE AS-S-UV | Witcom Engineering Plastics B.V. | HDPE | Witcom HDPE |
| NuSil MED-6010 | NuSil Technology | Silicone | NuSil |
| ALCUDIA® EVA PA-460 | REPSOL | EVA | ALCUDIA® EVA |
| Ethavin™ C85FRNC | Vi-Chem Corporation | TPO (POE) | Ethavin™ |
| MAJORIS EW886 | AD majoris | PP, Unspecified | MAJORIS |