| EPO-TEK® OM125 is two component, high Tg, optical epoxy designed for bonding multi-mode fiber optic connectors. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 80.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 2.8E-5 | cm/cm/°C | |
| -- 3 | 1.1E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Transmittance | |||
| 800 nm | > 97.0 | % | |
| 1000 nm | > 98.0 | % | |
| 1500 nm | > 96.0 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 3.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 367 | °C | TGA |
| Die Shear Strength - >20 kg (23°C) | 46.9 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 175 | °C | |
| Intermittent | -55 to 275 | °C | |
| Storage Modulus | 2.67 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.25 | % | |
| 250°C | 0.56 | % | |
| 300°C | 1.4 | % |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 4 | Blue | ||
| -- 5 | Clear/Transparent | ||
| Density | |||
| Part B | 0.988 | g/cm³ | |
| Part A | 1.16 | g/cm³ | |
| Viscosity 6(23°C) | 2.4 to 5.4 | Pa·s | |
| Curing Time (80°C) | > 1.0 | hr | |
| Pot Life | < 60 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 | ||
| Lap Shear Strength (23°C) | 5.57 | MPa | |
| Relative Permittivity (1 kHz) | 3.90 | ||
| Volume Resistivity (23°C) | < 2.0E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.019 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 50 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFILL H 15 S 40 T0 | RIALTI Srl | PP Homopolymer | RIALFILL |
| Radiflam® A RV350 HF 100 NAT 4570 | Radici Plastics | Nylon 66 | Radiflam® |
| Sarlink® TPV 3135 | Teknor Apex Company | TPV | Sarlink® TPV |
| RJM TPS-T 65A | RJM International, Inc. | TPE | RJM |
| EZPrene 9075A | ENPLAST Americas, a Ravago Group Company | TPV | EZPrene |