Borealis PE FT5236
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MGgHw1_Borealis-PE-FT5236.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FT5236 is a Low Density Polyethylene for Film Extrusion. Tubular Technology. Includes Anti-block and Medium Slip additives. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.20 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| secant modulus | ASTM D882A | ||
| MD : 40 µm, blown film | 230 | MPa | ASTM D882A |
| TD : 40 µm, blown film | 260 | MPa | ASTM D882A |
| Tensile Strength | ISO 527-3 | ||
| MD : 40 µm, blown film | 27.0 | MPa | ISO 527-3 |
| TD : 40 µm, blown film | 24.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 250 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 550 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 120 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm, blown film | 4.0 | N | ISO 6383-2 |
| TD : 40 µm, blown film | 2.0 | N | ISO 6383-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Multi-Axial Instrumented Impact Energy (0.0400mm, Blown Film, total impact penetration energy) | 2.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 112 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (40.0 µm, Blown Film) | 85 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Extrusion instructions |
|---|
| Draw Down: 30 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyre-ML® RC-5057 | Industrial Summit Technology Co. | API | Pyre-ML® |
| TECHNYL® eXten D 458P NATURAL | Solvay Engineering Plastics | Nylon 610 | TECHNYL® eXten |
| STYRON™ 650 HF | Trinseo | PS (GPPS) | STYRON™ |
| Ensinger TECACRYL® | Ensinger Inc. | Acrylic, Unspecified | Ensinger |
| Karina NATURAL PVC COMPOUND -E V-150 LT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |