Toyolac® AX05-X08
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MGNrNG_Toyolac-AX05-X08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® AX05-X08 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| 23°C | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 29 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 108 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 40.0 | MPa | ASTM D638 |
| 23°C | 42.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 20 | % | ASTM D638 |
| Break, 23°C | 15 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2000 | MPa | ASTM D790 |
| 23°C | 2010 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 60.0 | MPa | ASTM D790 |
| 23°C | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 30 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 440 | J/m | |
| 23°C, 12.7 mm | 270 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 84.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 79.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 90.0 to 95.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Kingfa JH710 G10 | Kingfa | PC Alloy | Kingfa |
| Hostaform® S 9364 XAP² ™ | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LG PMMA HI855H | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| Paracril® X3675 | INSA | NBR | Paracril® |
| Durethan® BKV 130 H2.0 DUS008 901510 | LANXESS GmbH | Nylon 6 | Durethan® |