Mecoline IS RDX 5243 F
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Melos GmbH |
| Trademark: | Mecoline |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MFtYTH_Mecoline-IS-RDX-5243-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| System cabling for military vehicles, aerospace, sensor technology, engine & transformer construction, automotive motor compartments and industrial automation and process controls. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.3 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 19 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 811-1-1 | ||
| -- 1 | 19.0 | MPa | |
| -- 2 | > 10.0 | MPa | |
| Tensile Strain | |||
| Break 3 | 400 | % | IEC 811-1-1 |
| Break 4 | > 600 | % | IEC 811-1-1 |
| Break, -50°C | > 30 | % | IEC 811-1-4 |
| Break, -40°C | > 150 | % | IEC 811-1-4 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Set 5 | IEC 540 | ||
| Elongation under load | 25 | % | |
| Residual elongation | 10 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 170 to 180 | °C | |
| Extruder Screw L/D Ratio | >24.0:1.0 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D2671 |
| Dielectric Constant (50 Hz) | 4.80 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 28 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 50.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 150 to 160 | °C | |
| Cylinder Zone 2 Temp. | 160 to 170 | °C | |
| Cylinder Zone 3 Temp. | 165 to 175 | °C | |
| Cylinder Zone 4 Temp. | 170 to 180 | °C | |
| Cylinder Zone 5 Temp. | 170 to 180 | °C | |
| Adapter Temperature | 170 to 180 | °C | |
| Die Temperature | 170 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | After crosslinking |
| 2 . | Before crosslinking |
| 3 . | After crosslinking |
| 4 . | Before crosslinking |
| 5 . | at 200°C/15min/0.2 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Romiloy® 1015/01 F | ROMIRA GmbH | PC+ABS | Romiloy® |
| Talcoprene® 540TC NAT | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Texalan® 3 Series 398A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 3 Series |
| Haysite Plastics ETS | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| Keyflex® BT 7038D | LG Chem Ltd. | TPC-ET | Keyflex® BT |