Order Products : sales@su-jiao.com
CYCOLOY™ MC8100 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MFRfOr_CYCOLOYMC8100resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/ABS, extrusion and blow molding grade. |
| General Information | |
|---|---|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2070 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 52.4 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 100 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2070 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 77.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 430 | J/m | ASTM D256 |
| 23°C | 530 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 47.5 | J | ASTM D3763 |
| 23°C, Total Energy | 54.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 124 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 104 | °C | ASTM D648 |
| CLTE - Flow (-40 to 40°C) | 8.1E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 99 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.050 | % | |
| Cylinder Zone 1 Temp. | 238 - 249 | °C | |
| Cylinder Zone 2 Temp. | 238 - 254 | °C | |
| Cylinder Zone 3 Temp. | 238 - 254 | °C | |
| Cylinder Zone 4 Temp. | 238 - 257 | °C | |
| Cylinder Zone 5 Temp. | 243 - 260 | °C | |
| Adapter Temperature | 243 - 260 | °C | |
| Die Temperature | 249 - 266 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 24 hrsExtruder Feed Zone Temperature: 60 - 79°CHead - Zone 6 - Top Temperature: 243 - 260 °CHead - Zone 7 - Bottom Temperature: 243 - 260 °CMelt Temperature (Parison): 243 - 260 °CMinimum Moisture Content: .04 %Mold Temperature: 38 - 88 °CScrew Speed: 20 - 50 rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F02-140A | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TECHNYL® A 216 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| U-polymer P-5001 | UNITIKA Plastics Division | Polyarylate | U-polymer |
| Escorene™ Ultra FL 00728CC | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Loyblend® TA-1004 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |