TRIBOCOMP® PEI TS0
| Category: | PEI , Polyether Imide |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MFOzQb_TRIBOCOMP-PEI-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® PEI TS0 is a Polyether Imide (PEI) product filled with 15% ptfe fiber. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.70 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield, 23°C | 85.0 | MPa | |
| Yield, 90°C | 80.0 | MPa | |
| Yield, 120°C | 70.0 | MPa | |
| Tensile Strain (Break, 23°C) | > 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 100 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| vs. Itself - Dynamic | 0.12 | ||
| vs. Itself - Static | 0.10 | ||
| Wear Factor | 40 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 195 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 6.0E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.16 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Electric Strength | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 350 to 370 | °C | |
| Cylinder Zone 2 Temp. | 360 to 390 | °C | |
| Cylinder Zone 3 Temp. | 370 to 390 | °C | |
| Cylinder Zone 4 Temp. | 380 to 410 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx TPP1B40 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Shinko-Lac® ABS VP-1 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| APEX® 88-N054-A | Teknor Apex Company | PVC, Flexible | APEX® |
| Geon™ Vinyl Wire & Cable WJAC31L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Huafon HF-3690A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |