ULTEM™ 2210EPR resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MFAkCD_ULTEM-2210EPR-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6890 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 138 | MPa | |
| Break | 138 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 3.0 | % | |
| Flexural Modulus | ASTM D790 | ||
| 100 mm Span 4 | 6890 | MPa | |
| 50.0 mm Span 5 | 6890 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Yield, 50.0 mm Span 6 | 207 | MPa | |
| Break, 100 mm Span 7 | 207 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 590 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 14.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 211 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm | 214 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 206 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 209 | °C | |
| Vicat Softening Temperature | 210 | °C | ASTM D1525 8 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 3.6E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.2E-5 | cm/cm/°C | |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI Str | 105 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 9 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.406 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | Rate B (120°C/h), Loading 2 (50 N) |
| 9 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66 BT LS | Plastcom | Nylon 66 | SLOVAMID® 66 |
| GAPEX® RPP20EB32BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| Eltex® P RF110 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | Eltex® P |
| INEOS Wire & Cable B24D760 | INEOS Olefins & Polymers Europe | EBA | INEOS Wire & Cable |
| Latiohm 66-08 PD02 G/35 | LATI S.p.A. | Nylon 66 | Latiohm |