LNP™ LUBRICOMP™ DFL36E compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MEQv1X_LNPLUBRICOMPDFL36Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DFL36E is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Easy Molding, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DFL-4036 EM Product reorder name: DFL36E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Fracture | 123 | MPa | ASTM D638 |
| Fracture 1 | 123 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Fracture | 2.4 | % | ASTM D638 |
| Fracture 2 | 2.4 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 50.0mm span 3 | 9380 | MPa | ASTM D790 |
| -- | 9380 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- | 188 | MPa | ASTM D790 |
| Fracture, 50.0mm span 4 | 188 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 690 | J/m | ASTM D4812 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7600 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Teflon® FEP 9835 | DuPont Fluoropolymers | FEP | Teflon® FEP |
| Kumho EP HAC 8250W | Korea Kumho Petrochemical Co., Ltd. | PC+ABS | Kumho EP |
| ESTOPLAST EP 1500BB11DP | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| Durez® 33015 | SBHPP | Phenolic | Durez® |