VENYL ZG108 - 8121
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MDteyF_VENYL-ZG108---8121.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL ZG108 - 8121 is a Polyamide 66/6 Copolymer (Nylon 66/6) product filled with 15% glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 to 0.90 | -- | % | Internal Method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5600 | 3800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 125 | 65.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | 3.0 | 5.0 | % | |
| Break | 4.0 | 8.0 | % | |
| Flexural Modulus | 4500 | 2900 | MPa | ISO 178 |
| Flexural Stress | 155 | 95.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 30 | 40 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 242 | -- | °C | ISO 3146 |
| CLTE - Flow | 4.0E-5 | -- | cm/cm/°C | ASTM E831 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Oxygen Index | 21 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 250 to 265 | °C | |
| Front Temperature | 250 to 265 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 80.0 to 110 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 | RTP Company | Acetal (POM) Copolymer | RTP |
| Spartech Polycom PP5230 | Spartech Polycom | PP Homopolymer | Spartech |
| Texalan® 5 Series 598A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 5 Series |
| Hylon® N1033TL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| 3M™ Dyneon™ Fluoroelastomer FE 5623 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |