WINDFORM® LX 2.0
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | CRP Technology s.r.l. |
| Trademark: | WINDFORM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MDhIIT_WINDFORM-LX-2-0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Technology: Selective Laser Sintering Windform® LX 2.0 has improved the already excellent performances of Windform® LX and this can be noticed from technical properties and sinterability point of view. Windform® LX 2.0 is a new polyamide based material reinforced with new generation glass fibre system. The properties of Windform® LX 2.0 make it particularly suited for functional applications and finished complex parts. Windform® LX 2.0 is a naturally black material and is characterised by improved Ultimate Tensile Strength (UTS), increased stiffness as well as a high level of resistance to temperature, while providing an attractive surface finish. Windform® LX 2.0 also underlines its advantage towards Windform® GF, PRO and PRO B, with an excellent rate between quality and price. Windform® LX 2.0 is perfect to create functional prototypes or finished parts that require reliability, good temperature resistance and a captivating matt black colour. Applications: There are several fields of application: covers, latching systems, air intake systems, connectors, applications for drivers cockpit (e.i. steering wheel-mounted paddle shifters), but also cooling/ducted fans, UAV structural components, sport functional prototypes, performing design parts and stiff pieces for packaging, and other applications in the naval and aerospace industries. Surface Finish: After SLS Process 7.5 Ra After finishing (CNC machining) 1.5 Ra |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.31 | g/cm³ |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6250 | MPa | ISO 527-2 |
| Tensile Stress | 59.9 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2 |
| Flexural Modulus | 4860 | MPa | ISO 14125 |
| Flexural Stress | 92.2 | MPa | ISO 14125 |
| Tensile Modulus - per density unit | 4770 | MPa/g/cm³ | |
| Ultimate Tensile Strength - per density unit | 45.7 | MPa/g/cm³ |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.4 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 18 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 176 | °C | ASTM D648 |
| Vicat Softening Temperature | 178 | °C | ASTM D1252 1 |
| Melting Temperature | 180 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sizzle™ HHLM | Plastic Selection Group, Inc. | PS (GPPS) | Sizzle™ |
| STYRON A-TECH™ 1110 | Trinseo | PS (HIPS) | STYRON A-TECH™ |
| Bynel® 1123 | DuPont Packaging & Industrial Polymers | EVA | Bynel® |
| APEX® 3601-75 | Teknor Apex Company | PVC, Flexible | APEX® |
| Gallonprene® GP520-9516 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |