Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
Manufacturer: | LG Chem Ltd. |
Trademark: | Lucene™ |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | MDCdcY_Lucene-LC165.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Applications:
Performance:
Description: LC165 is an ethylene-1-butene copolymer produced using LG Chem's metallocene polymerization catalyst and solution process technology. This resin is an excellent impact modifier for plastics and offers unique performance capabilities for compounded products. |
General Information | |
---|---|
Features |
|
Uses |
|
Forms |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 0.862 | g/cm³ | ASTM D1505 |
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
Mooney Viscosity (ML 1+4, 121°C) | 32 | MU | ASTM D1646 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Durometer Hardness (Shore A) | 43 | ASTM D2240 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength 1(Break) | 2.20 | MPa | ASTM D638 |
Tensile Elongation 2(Break) | > 800 | % | ASTM D638 |
Flexural Modulus - 1% Secant | 9.00 | MPa | ASTM D790 |
Elastomers | Nominal Value | Unit | Test Method |
---|---|---|---|
Tear Strength 3 | 17.0 | kN/m | ASTM D624 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Glass Transition Temperature | -58.0 | °C | Internal Method |
Melting Temperature | 30.0 | °C | Internal Method |
Note Message | |
---|---|
1 . | 510 mm/min |
2 . | 510 mm/min |
3 . | Die C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
RTP 200 GB 20 | RTP Company | Nylon 66 | RTP |
Medalist® MD-150 | Teknor Apex Company | TPE | Medalist® |
Generic PBT+PET - Glass Fiber | Generic | PBT+PET | Generic |
Kuraray Poval® PVA 117 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
SCHULABLEND® SCHULABLEND® (ABS/PA) M/MK 7102 GF20 | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |