Amodel® HFZ A-4133L
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Amodel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MCF7Lg_Amodel-HFZ-A-4133L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Amodel HFZ A- 4133 L polyphthalamide (PPA) is a 33% glass fiber reinforced, hot water moldable resin. The main properties include heat resistance, reduced gas emission over a wide temperature range, high strength and rigidity, low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel HFZ A- 4133 L resin is ideal for automotive electrical and electronic products, including connectors, sockets, switches and sensors. It is also a good choice for protecting key control systems under the hood, such as anti-lock braking system, traction control system, steering system, engine electronic control, transmission and chassis control unit. -Black: HFZ A- 4133 L BK 324
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.26 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2 |
| Flexural Modulus | 11000 | MPa | ISO 178 |
| Flexural Stress | 255 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.2 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | 8.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 310 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 327 | °C | ISO 3146 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : 0 to 90°C | 2.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 150 to 250°C | 1.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 0 to 90°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 150 to 250°C | 1.5E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.90 | ASTM D150 | |
| 1 MHz | 3.70 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 6.0E-3 | ASTM D150 | |
| 1 MHz | 0.016 | ASTM D150 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Resistance to Ignition (HVAR) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1(0.800 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | 800 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 800 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.045 | % | |
| Rear Temperature | 318 - 324 | °C | |
| Front Temperature | 327 - 332 | °C | |
| Processing (Melt) Temp | 329 - 343 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C |
| Injection instructions |
|---|
| 射出压力：3~4英寸/秒 |
| Note Message | |
|---|---|
| 1 . | These flammability ratings do not represent the risk of these materials or any other materials in actual fire situations. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bormed™ HJ875MO | Borealis AG | PP Homopolymer | Bormed™ |
| ECOGRAN® PSCI BLK | Eurocompound Polymers | PS (HIPS) | ECOGRAN® |
| EcoLon® MRGF1914-BK1 | Wellman Engineering Resins | Nylon 66 | EcoLon® |
| Sylvin 8354-62D Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 6185-80 White 1118 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |