Promyde B30 P2 G30 is a Polyamide 6 UL certified injection moulding grade with 30% glass fibre and heat stabilized.

CHARACTERISTICS
Promyde B30 P2 G30 is distinguished by high mechanical strength, hardness, rigidity, thermo stability (melting point 220°C), and resistance to hot lubricants and water. Parts made from Promyde B30 P2 G30 have particularly high dimensional stability and creep strength.

APPLICATIONS
Promyde B30 P2 G30 is used in a wide range of applications where a combination of mechanical properties and thermal resistance is needed.

Glass-fibre reinforced grades are suitable for housings, supports, industrial articles and electrical insulating parts.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	heat stabilizer
Features	Good dimensional stability Rigidity, high High strength Insulation Good creep resistance Thermal Stability Thermal stability, good High hardness
Uses	Electrical components Electrical housing Industrial application Insulating material Shell
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density (23°C)	1.36	--	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)	45.0	--	cm³/10min	ISO 1133
Molding Shrinkage
Vertical flow direction	0.40 - 0.45	--	%
Flow direction	0.30 - 0.35	--	%
Water Absorption				ISO 62
Saturated, 23°C	6.7	--	%	ISO 62
Equilibrium, 23°C, 50% RH	2.1	--	%	ISO 62
Viscosity Number	145	--	cm³/g	ISO 307

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	9300	6200	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	190	110	MPa	ISO 527-2/50
Nominal Tensile Strain at Break (23°C)	3.0	5.0	%	ISO 527-2/50
Flexural Modulus ¹(23°C)	8000	5100	MPa	ISO 178
Flexural Stress ²(23°C)	250	180	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	10	--	kJ/m²	ISO 179/1eA
23°C	13	25	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	75	--	kJ/m²	ISO 179/1eU
23°C	85	95	kJ/m²	ISO 179/1eU

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	215	--	°C	ISO 75-2/B
1.8 MPa, not annealed	210	--	°C	ISO 75-2/A
Melting Temperature (DSC) ³	222	--	°C	ISO 3146
Linear thermal expansion coefficient				ISO 11359-2
Flow : 23 to 80°C	2.0E-5	--	cm/cm/°C	ISO 11359-2
Lateral : 23 to 80°C	6.0E-5	--	cm/cm/°C	ISO 11359-2

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+13	1.0E+10	ohms	IEC 60093
Volume Resistivity	1.0E+15	1.0E+12	ohms·cm	IEC 60093
Dielectric Constant (1 MHz)	3.80	6.80		IEC 60250
Dissipation Factor (1 MHz)	0.023	0.22		IEC 60250
Comparative Tracking Index	500	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (1.50 mm)	HB	--		UL 94

Injection	Dry	Unit
Drying Temperature	< 80.0	°C
Drying Time	4.0 - 6.0	hr
Processing (Melt) Temp	250 - 270	°C
Mold Temperature	40.0 - 80.0	°C
Injection Rate	Moderate-Fast

Injection instructions
Back Pressure: moderate

Note Message
1 .	2.0 mm/min
2 .	2.0 mm/min
3 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Santoprene™ 8211-75	ExxonMobil Chemical	TPV	Santoprene™
Spartech Polycom SS1080U	Spartech Polycom	ASA	Spartech
Vydyne® R228	Ascend Performance Materials Operations LLC	Nylon 66	Vydyne®
DOW™ Electrical & Telecommunications HFDK-0586 BK	The Dow Chemical Company	Ethylene Copolymer	DOW™ Electrical & Telecommunications
Pujie CM35H	Zhanhua Pujie Chemical Technology Co.,Ltd	CPE	Pujie