Staramide 6 1565VE11
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MAeULk_Staramide61565VE11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide 6 1565VE11 is a High Density Glass Fiber Reinforced Polyamide 6 Injection Molding Resin with Improved Thermal Conductivity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 3.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage (3.00 mm) | 0.20 - 0.40 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 5800 | MPa | ISO 178 |
| Flexural Stress | 123 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 23 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 224 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 250 - 280 | °C | |
| Front Temperature | 250 - 280 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 50 - 90 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecodur® PB70 GR30 NL100 IL | Eurotec Engineering Plastics | PBT | Tecodur® |
| Borlink™ LE0511 | Borealis AG | PE, Unspecified | Borlink™ |
| Ferro PP LPP20BN51AL | Ferro Corporation | PP, Unspecified | Ferro PP |
| Iupilon® ECF2030R | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| MAJORIS AFR992 - 8229 | AD majoris | PP Copolymer | MAJORIS |