Grilon® F 50 nat 6368
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MA7du4_Grilon-F-50-nat-6368.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilon® F 50 nat 6368 is a Polyamide 6 (Nylon 6) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for blow molding, blown film, extrusion, or injection stretch blow molding. Important attributes of Grilon® F 50 nat 6368 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/21.6 kg) | 45.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 750 | MPa | ISO 527-2 |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-3 | |||
| MD : Yield | 35.0 | -- | MPa | |
| TD : Yield | 30.0 | -- | MPa | |
| MD : Break | 100 | -- | MPa | |
| TD : Break | 90.0 | -- | MPa | |
| Tensile Elongation | ISO 527-3 | |||
| MD : Yield | 15 | -- | % | |
| TD : Yield | 15 | -- | % | |
| MD : Break | 700 | -- | % | |
| TD : Break | 700 | -- | % | |
| Elmendorf Tear Strength | ISO 6383-2 | |||
| MD | 10 | -- | N | |
| TD | 10 | -- | N | |
| Trouser Tear Resistance | ISO 6383-1 | |||
| MD | 30.0 | -- | N/mm | |
| TD | 30.0 | -- | N/mm | |
| Water Vapor Transmission Rate (23°C, 85% RH) | 15 | -- | g/m²/24 hr | DIS 15106-1/-2 |
| Oxygen Transmission Rate | DIS 15105-1/-2 | |||
| 23°C 1 | 25 | -- | cm³/m²/bar/24 hr | |
| 23°C 2 | 50 | -- | cm³/m²/bar/24 hr | |
| Carbon Dioxide Transmission Rate | DIS 15105-1/-2 | |||
| 23°C 3 | 250 | -- | cm³/m²/bar/24 hr | |
| 23°C 4 | 80.0 | -- | cm³/m²/bar/24 hr |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Gelboflextest | 900 | -- | holes/m² | Internal Method |
| ISO Type | PA 6, F, 34-030 | -- | ISO 1874 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 5.0 | kJ/m² | |
| 23°C | 6.0 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 5 | 222 | -- | °C | ISO 11357-3 |
| Optical | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Gloss (60°) | 100 | -- | ISO 2813 |
| Note Message | |
|---|---|
| 1 . | 0% RH |
| 2 . | 85% RH |
| 3 . | 85% RH |
| 4 . | 0% RH |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PC 93 T 30 | Plastcom | PP, Unspecified | SLOVALEN® |
| DENYL 6 0037 ST | Vamp Tech | Nylon 6 | DENYL |
| LEXAN™ ML7686 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Lushan PF-300 | Guangzhou Lushan New Materials Co., Ltd | Polyolefin, Unspecified | Lushan |
| Sylvin 8387-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |