Order Products : sales@su-jiao.com
Lionpol HF-206001
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Lion Polymers Incorporated |
| Trademark: | Lionpol |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M9sGRE_Lionpol-HF-206001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lionpol HF-206001 is a thermoplastic elastomer (TPE) product,. It is available in North America. The main characteristics are: high liquidity. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 62 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 2.1 - 3.5 | % | ASTM D955 |
| Transverse flow | 2.1 - 3.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 1 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 0.103 | MPa | ASTM D412 |
| Tensile Strength (Break) | 1.10 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1200 | % | ASTM D412 |
| Additional Information |
|---|
| Permanent Set: 9% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 141 - 179 | °C | |
| Front Temperature | 163 - 202 | °C | |
| Nozzle Temperature | 163 - 202 | °C | |
| Mold Temperature | 21.1 - 32.2 | °C | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Compound 822 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| ALTECH® PP-H B 4930/506 MR30 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| DESLON™ 6 DSC102VG7 | DESCO Co., Ltd. | Nylon 6 | DESLON™ 6 |
| Ferro PP TPP20AN05BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Karina BLACK PVC COMPOUND -E 855-48/ 1-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |