XANTAR® XRM 1006
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | XANTAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M9Rzgw_XANTAR-XRM-1006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact Modified, Flame Retardant, Good Flow |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.80 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.35 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -40°C | 30 | kJ/m² | |
| -30°C | 45 | kJ/m² | |
| -20°C | 60 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 60.0 | J | |
| 23°C | 60.0 | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 6000 | N | |
| 23°C | 5500 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| Ball Pressure Test (140°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 2.90 | ||
| 1 MHz | 2.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 6.6E-4 | ||
| 1 MHz | 9.2E-3 | ||
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 2.50 mm | V-0 5VB | ||
| 1.50 mm | V-1 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 2.00 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 2.00 mm | 850 | °C | |
| 3.00 mm | 875 | °C |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity of Melt | 0.26 | W/m/K |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SV956 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| Termaloy L-8040 | Proquigel | PC+ABS | Termaloy |
| BJB Polyurethane TC-812 A/B LIGHTCAST | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| ALTECH® PP-H B 4930/506 MR30 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Fainplast PVC FK 0635 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |