Witcom PC 2C-FR-MR
| Category: | PC , Polycarbonate |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M8qY4i_Witcom-PC-2C-FR-MR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PC 2C-FR-MR is a polycarbonate (PC) product that contains 10% carbon fiber reinforcement. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.10 - 0.30 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 - 3.0 | % | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 7.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 140 | °C | ISO 75-2/A |
| CLTE - Flow | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 - 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 - 320 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil MED-6010 | NuSil Technology | Silicone | NuSil |
| Badamid® PA610 GF50 | Bada AG | Nylon 610 | Badamid® |
| Forprene® 6NM919A60 | SO.F.TER. SPA | TPV | Forprene® |
| Kepital® F20-03 M | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| LNP™ THERMOCOMP™ PX01658 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |