IPC PP 4833H-T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | International Polymers Corporation |
| Trademark: | IPC PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M8VqNG_IPC-PP-4833H-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IPC PP 4833H-T is a polypropylene homopolymer (PP Homopoly) material, which contains 33% talc filler. This product is available in North America,. The main characteristics of IPC PP 4833H-T are: homopolymer. The typical application field of IPC PP 4833H-T is: automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 29.0 | MPa | ISO 527-2 |
| Flexural Modulus | 3100 | MPa | ISO 178 |
| Shear Modulus | 1100 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 2.7 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 119 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 69.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Filler Content: 31 to 35% TalcMelt Mass-Flow Rate, ISO 1133, 230°C, 2.16kg: 12.0 to 18.0 g/10 minDensity - Specific Gravity, ISO 1183 (A): 1.12 to 1.16 g/cm³The value listed as Shear Modulus, ASTM D732, was tested in accordance with ASTM D4065.The value listed as Mold Shrinkage, ISO 294-4 was tested in accordance with ISO 2577. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 83MF90 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Stanyl® TW271F6J10 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| ASI POLYPROPYLENE PP 3369-01 | A. Schulman Inc. | PP Homopolymer | ASI POLYPROPYLENE |
| HANWHA 7600 | Hanwha Chemical | HDPE | HANWHA |
| O'Tech OM 5531 | O'Tech Corporation | PVC, Unspecified | O'Tech |