Epoxies, Ect. 50-3112
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxies, Etc. |
| Trademark: | Epoxies, Ect. |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M8S9DC_Epoxies-Ect-50-3112.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
50-3112 is a two component fast curing thermally conductive epoxy adhesive. This product was specifically formulated for use in the convenient TriggerBond® dual barrel cartridge system. 50-3112 has a simple 1:1 mix ratio and develops a 1,400 psi Lap Shear strength (aluminum to aluminum) in four hours at room temperature. After just twenty four hours the strength is over 2,200 psi. 50-3112 offers fast heat dissipation for a wide range of electronic applications. The black resin and white hardener provide an excellent visual indication of a complete mix. Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | |||
| -- 1 | 4.5E-5 | cm/cm/°C | |
| -- 2 | 1.8E-4 | cm/cm/°C | |
| Thermal Conductivity | 1.0 | W/m/K |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Operating Temperature | -40.0 to 120 | °C |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 3 | Black | ||
| -- 4 | Grey | ||
| -- 5 | White | ||
| Density | |||
| 25°C 6 | 1.50 | g/cm³ | |
| 25°C 7 | 1.50 | g/cm³ | |
| Viscosity | |||
| 25°C 8 | 70 | Pa·s | |
| 25°C 9 | 70 | Pa·s | |
| Curing Time (23°C) | 1.0 to 2.0 | hr | |
| Gel Time 10(25°C) | 15 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness | |||
| Shore D, 70°C | 50 | ||
| Shore D, 25°C | 80 | ||
| Lap Shear Strength | |||
| -- 11 | 15.4 | MPa | |
| -- 12 | 9.74 | MPa | |
| Electric Strength | 17 | kV/mm | |
| Relative Permittivity (100 Hz, 25°C) | 5.30 | ||
| Volume Resistivity (25°C) | 2.4E+12 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Below Tg |
| 2 . | Above Tg |
| 3 . | Part A |
| 4 . | Mixed |
| 5 . | Part B |
| 6 . | Part B |
| 7 . | Part A |
| 8 . | Part B |
| 9 . | Part A |
| 10 . | 15 grams |
| 11 . | Al to Al, After 24 hours |
| 12 . | Al to Al, After 4 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hifax TYC 1168X | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| IROGRAN® A 60 E 4902 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| ISPLEN® PM 364 AT | REPSOL | PP Copolymer | ISPLEN® |
| PEXLOY™ PXP-315UV-BK10 | Pier One Polymers, Inc. | PC+Polyester | PEXLOY™ |
| Domamid HT™ 7750R15F4H3 Bk-598 | Technical Polymers, LLC | Nylon 66 | Domamid HT™ |