LNP™ THERMOCOMP™ UF006AS compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M82XyE_LNP-THERMOCOMP-UF006AS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* UF006AS is a compound based on Polyphthalamide resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound UF-1006 A HS Product reorder name: UF006AS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 | % | ASTM D955 |
| Across Flow : 24 hr | 0.97 | % | ISO 294-4 |
| Flow : 24 hr | 0.24 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.22 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.42 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11600 | MPa | ASTM D638 |
| -- | 14800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 183 | MPa | ASTM D638 |
| Break | 167 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.9 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 11500 | MPa | ASTM D790 |
| -- | 11200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 254 | MPa | ASTM D790 |
| -- | 255 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 410 | J/m | ASTM D4812 |
| 23°C 3 | 31 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.93 | J | ASTM D3763 |
| -- | 1.48 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 282 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 260 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 HF UV PRTA010 NR311 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| IROGRAN® A 98 E 4066 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Karina BLACK PVC COMOUND 501D48/ 1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYfill PPH TS15010 H VTUV1 | Polykemi AB | PP Homopolymer | POLYfill |
| NILAMID® XS3 GF55 TF10 | Nilit Plastics | Nylon, Unspecified | NILAMID® |