Polygrade® PET B3 G45 PRTA011 PG302
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Polygrade® PET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M6GQEq_Polygrade-PET-B3-G45-PRTA011-PG302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polygrade®PET B3 G45 PRTA011 PG302 is a polyethylene terephthalate (PET) material, which contains a 45% glass fiber reinforced material. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Polygrade®The main characteristics of PET B3 G45 PRTA011 PG302 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 - 1.71 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.15 - 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 185 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 15100 | MPa | ASTM D790 |
| Flexural Strength | 280 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 225 | °C | ASTM D696 |
| Melting Temperature | 255 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | > 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1385 TFE 10 | RTP Company | PPS | RTP |
| Generic MMBS | Generic | MMBS | Generic |
| LARIPUR® LPR 8020 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| Paxon™ BA54-030 | ExxonMobil Chemical | HDPE Copolymer | Paxon™ |
| Pinnacle PP 1335 Z | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |